Unique Key Features
EDHMR is manufactured using hardwood and its density is over 820 kg/m3. It has a uniform density gradient and a compact core which gives it the best routing characteristics. The main highlight of this product is its uniform thickness and homogeneous structure.
Strength and Durability
The extreme density and compact structure of EDHMR results in improved strength and durability compared to other wood-based materials. It can withstand heavy loads and is less prone to warping or bending.
Smooth Surface
EDHMR has a smooth and uniform surface, making it an excellent choice for applications where a refined and consistent finish is desired.
Versatility
EDHMR can be used for a wide range of applications, including furniture components, cabinet doors, moldings, wall panels, laminated flooring, and various other interior and structural elements.
Laminate and Veneer Applications:
The smooth surface of EDHMR makes it suitable for laminate and veneer applications, enabling the creation of visually appealing and durable finishes.
Substrate Material
EDHMR is commonly used as a substrate for high-pressure laminate (HPL) and other decorative surfacing materials due to its strength and stability.
Eco-Friendly
Furniture made from EDHMR is low in emission and eco-friendly too. Like other engineered wood products, EDHMR is made from recycled wood fibers and can be sourced from sustainable forestry practices, making it an environment friendly option.
3, 5.5, 7.5, 11, 16, 16.75, 18, 25
8 x 4 (2440mm x 1220mm)
OSB (One side balancing)
BSB (Both side balancing)
OSL (One side laminated)
BSL (Both side laminated)
OSD (One side decorative)
Suede/Matt
S. NO | PARTICULARS | UNIT | IS:12406 HDF GRADE-1 SPECIFICATION | EDHMR (ACHIVED VALUE) |
---|---|---|---|---|
1 | Density | Kg/cum | 800 to 900 | 825 to 900 |
2 | Moisture Content | % | 5 to 10 | 5.24 |
3 | Water Absorption | |||
3.1 | After 2 hrs. soaking | % | 6 | 4.57 |
3.2 | After 24 hrs. soaking | |||
Up to & including 6.0 mm | % | 30 | ||
7.0 to 12.0 mm | % | 20 | 18.59 | |
13.0 to 19.0 mm | % | 13 | 11.46 | |
20.0 mm and above | % | 12 | ||
4 | Swelling in Water after 24 hrs. soaking | |||
4.1 | Thickness | % | 7 | 5.97 |
4.2 | Length and Width | % | 0.3 | 0.19 |
5 | Due to Surface Absorption in thickness after 2 hrs. soaking | % | 4 | 0.91 |
6 | Modulus of Rupture Avg. | N/sqmm | 32 to 35 | 35.32 |
7 | Modulus of Elasticity Avg. | N/sqmm | 3200 | 3422 |
8 | Internal Bond Avg. | |||
8.1 | Up to 20 mm | N/sqmm | 0.9 | 1.3 |
8.2 | Above 20 mm | N/sqmm | 0.8 | |
9 | Internal Bond after AWR Avg. | N/sqmm | 0.3 | 0.31 |
10 | Screw Withdrawal Strength | |||
10.1 | Face | N | 1500 | 2698 |